Columnar structure of reactively sputtered aluminium nitride films
Published 2002 · Chi-San Chen, Bing-Hwai Hwang, Hong-Yang Lu and Tzu-Chien Hsu
Journal of Physics D: Applied Physics
0
Citations
0
Influential Citations
Abstract
Columnar structure of thin aluminium nitride (AlN) films is examined by x-ray diffractometry (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The films were deposited on SiO2/Si(100) substrate using radiofrequency reactive sputtering method. Strong [0001] preferred orientation is observed by XRD and confirmed by selected area diffraction pattern of TEM. Columnar grains of ∼50–100 nm inclined at an angle of ∼10° to the substrate normal are observed by SEM. As revealed by TEM, each columnar grain is composed of nano-grains of the order of 10 nm and no faceting is observed in the nano-grains and columns. The [0001] preferred orientation results as columnar grains are oriented at various azimuthal angles with their c-axes perpendicular to the substrate surface. A slight tilt of a few tenths of a degree between adjacent nano-grains within a column is also observed. The random azimuthal orientation of columnar grains and small tilt between nano-grains in the films are accommodated by the amorphous phase present in the grain boundaries.