Huadong Tang, Jianbin Tang, Shijie Ding
Apr 1, 2005
Citations
1
Influential Citations
133
Citations
Quality indicators
Journal
Journal of Polymer Science Part A
Abstract
Polymeric forms of ionic liquids have many potential applications because of their high thermal stability and ionic nature. Two ionic liquid monomers, 1-(4-vinylbenzyl)-3-butyl imidazolium tetrafluoroborate (VBIT) and 1-(4-vinylbenzyl)-3- butyl imidazolium hexafluorophosphate (VBIH), were synthesized through the quaternization of N-butylimidazole with 4-vinylbenzylchloride and a subsequent anion- exchange reaction with sodium tetrafluoroborate or potassium hexafluorophosphate. Copper-mediated atom transfer radical polymerization was used to polymerize VBIT and VBIH. The effects of various initiator/catalyst systems, monomer concentrations, solvent polarities, and reaction temperatures on the polymerization were examined. The polymerization was well controlled and exhibited living characteristics when CuBr/1,1,4,7,10,10-hexamethyltriethylenetetramine or CuBr/2,2′-bipyridine was used as the catalyst and ethyl 2-bromoisobutyrate was used as the initiator. Characterizations by thermogravimetric analysis, differential scanning calorimetry, and X-ray diffraction showed that the resulting VBIT polymer, poly[1-(4-vinylbenzyl)-3-butyl imidazolium tetrafluoroborate] (PVBIT), was amorphous and had excellent thermal stability, with a glass-transition temperature of 84 °C. The polymerized ionic liquids could absorb CO2 as ionic liquids: PVBIT absorbed 0.30% (w/w) CO2 at room temperature and 0.78 atm. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 1432–1443, 2005