T. Kikuchi, Osamu Nishinaga, S. Natsui
Feb 20, 2015
Citations
0
Influential Citations
82
Citations
Quality indicators
Journal
Electrochimica Acta
Abstract
Abstract Highly ordered anodic porous alumina with a large-scale cell diameter was successfully fabricated via anodizing in a new electrolyte, etidronic acid (1-hydroxyethane-1,1-diphosphonic acid). High-purity aluminum specimens were anodized in a 0.3 M etidronic acid solution under constant current density and voltage conditions. Etidronic acid anodizing at 210 to 270 V at the appropriate temperature caused the anodic porous alumina to exhibit self-ordering behavior, and periodic nanostructures measuring 530 to 670 nm in cell diameter were fabricated on the aluminum substrate. The self-ordering voltage and the corresponding cell diameter could be increased without burning by systematically increasing the stepwise voltage. Two-step etidronic acid anodizing without nanoimprinting can easily yield the formation of highly ordered anodic porous alumina with a large-scale cell diameter. A submicrometer-scale dimple array fabricated via etidronic acid anodizing and subsequent selective oxide dissolution gave rise to bright structural color with a rainbow distribution.