A. Rojas, D. Cerro, A. Torres
Sep 1, 2015
Citations
2
Influential Citations
51
Citations
Journal
Journal of Supercritical Fluids
Abstract
Abstract The impregnation of active compounds in polymeric matrices using supercritical carbon dioxide (scCO 2 ) is a well-known technique, which is currently used to formulate controlled drug release materials. In this study, supercritical impregnation of 2-nonanone in linear low-density polyethylene (LLDPE) was done in order to prepare active polymer films to be used in food packaging. Impregnation tests were carried out in a high-pressure cell, at 313 K with pressures ranging from 12 to 22 MPa and at two different depressurization rates: 1.0 and 10.0 MPa min −1 . This procedure allowed the preparation of films containing 2-nonanone at concentrations varying from 0.21 to 0.34 w/w%. Higher concentrations of 2-nonanone in LLDPE were obtained for impregnations done at lower pressures and the lowest depressurization rate. Release experiments showed that the depressurization rate of the impregnation process is a key parameter, which significantly affects the initial content of the active compound in the polymer. Simultaneously, a phenomenological mass transfer model has been used to describe the release of 2-nonanone from the polymer to a food simulant. This model was used to correlate the experimental release kinetic data, obtaining the values of diffusion coefficient of 2-nonanone in LLDPE, which were quantified between 3.0 × 10 −12 and 3.6 × 10 −12 m 2 s −1 when depressurization rate was 10.0 MPa min −1 and 6.8 × 10 −12 m 2 s −1 when its value was 1.0 MPa min −1 .