R. Lenz, J. Sutherland, L. Westfelt
Mar 1, 1976
Citations
0
Influential Citations
12
Citations
Journal
Macromolecular Chemistry and Physics
Abstract
Under identical conditions of cationic polymerization at low temperature 2-(p-tolyl)-1-propene (α,p-dimethylstyrene) gave polymers with much higher syndiotactic contents than unsubstituted α-methylstyrene. All samples of poly(α,p-dimethylstyrene) were crystalline, but poly(α-methylstyrene) did not crystallize even at high degrees of stereoregularity. Similarly polymers of p-isopropyl-α-methylstyrene were crystalline, and the crystalline properties of copolymers of the three monomers were investigated and compared to those of the homopolymers. The roles of stereoregularity and crystallizability in forming crystalline products were considered. Unter identischen Bedingungen der kationischen Polymerisation bei tiefer Temperature lieferte 2-(p-Tolyl)-1-propen (α,p-Dimethylstyrol) Polymere mit hoherem syndiotaktischem Gehalt als das unsubstituierte α-Methylstyrol. Samtliche Proben von Poly(α,p-dimethylstyrol) erwiesen sich als kristallin im Gegensatz zum Poly(α-methylstyrol), das selbst bei hoher Stereoregularitat nicht kristallisierte. Ahnlich erwiesen sich Polymere des p-Isopropyl-α-methylstyrols als kristallin. Die kristallinen Eigenschaften von Copolymeren der drei Monomere wurden untersucht und mit denen der Homopolymere verglichen. Die Rolle der Stereoregularitat und der Kristallisierbarkeit bei der Bildung kristalliner Produkte wurde in Betracht gezogen.